Specific Process Knowledge/Characterization/XPS/Processing/Basics/3fitting: Difference between revisions
No edit summary |
No edit summary |
||
| Line 3: | Line 3: | ||
<!--Checked for updates on 5/10-2020 - ok/jmli --> | <!--Checked for updates on 5/10-2020 - ok/jmli --> | ||
<!--Checked for updates on 30/7-2018 - ok/jmli --> | <!--Checked for updates on 30/7-2018 - ok/jmli --> | ||
<!--Checked for updates on 9/5-2023 - ok/jmli --> | |||
{{Contentbydryetch}} | |||
== Fitting the oxygen O1s core level == | == Fitting the oxygen O1s core level == | ||
Latest revision as of 09:11, 9 May 2023
Feedback to this page: click here
Unless otherwise stated, the content of this page was created by the dry etch group at DTU Nanolab
Fitting the oxygen O1s core level
There is a few choices to make on the fitting of the O1s level. The level is an s-orbital and thus gives rise to a peak that is symmetric so any non-symmetric appearance must be caused several states of oxygen. The question is then to which states of oxygen they should be attributed. Below are shown the spectra of levels 0 (surface), 11 and 20.
We can establish that
- The main peak remains at fixed binding energy, and
- There is a shoulder at higher binding energy