Specific Process Knowledge/Thin film deposition/Deposition of Nickel

Feedback to this page: click here

Nickel deposition

Nickel can be deposited by e-beam evaporation, sputtering or electroplating. In the chart below you can compare the different deposition equipment.

• Electroplating of nickel
• Stress in Wordentec Ni films: study here.

	E-beam evaporation (Temescal)	E-beam evaporation (Wordentec)	E-beam evaporation (Physimeca)	Sputter deposition (Lesker)	Sputter deposition (Cluster-based sputter system)	Electroplating (Electroplating-Ni)
General description	E-beam deposition of Nickel	E-beam deposition of Nickel	E-beam deposition of Nickel	Sputter deposition of Nickel	Sputter deposition of Nickel	Electroplating of Nickel
Pre-clean	Ar ion bombardment	RF Ar clean		RF Ar clean	RF Ar clean	None
Layer thickness	10 Å to 1 µm *	10 Å to 1 µm *	10 Å to 2000 Å	10 Å to 5000 Å **	10 Å to 5000 Å **	~ 20 µm to ~ 1000 µm
Deposition rate	2-10 Å/s	10-15 Å/s	1-10 Å/s	Depends on process parameters, about 1 Å/s	Depends on process parameters	~ 10-250 Å/s
Batch size	Up to 4x6" wafers Up to 3x8" wafers (ask for holder) Many smaller pieces	24x2" wafers or 6x4" wafers or 6x6" wafers	1x 2" wafer or 1x 4" wafers or Several smaller pieces	Pieces or 1x4" wafer or 1x6" wafer	Up to 10x4" or 6" wafers Many smaller pieces	1x2" wafer or 1x4" wafer or 1x6" wafer
Allowed materials	Silicon Silicon oxide Silicon (oxy)nitride Photoresist PMMA Mylar Metals See also the cross-contamination sheet	Silicon Silicon oxide Silicon nitride Silicon (oxy)nitride Photoresist PMMA Mylar SU-8	Silicon Silicon oxide Silicon (oxy)nitride Photoresist PMMA Mylar SU-8 Metals	Silicon Silicon oxide Silicon (oxy)nitride Photoresist Metals	Almost any that do not outgas. Check the cross-contamination sheets in Labmanager.	Base materials: Silicon Polymers with Tg > 75°C Metals (bulk) Cross-linked or hard baked resists supported by one of the above mentioned materials Seed metals: NiV (75 - 100 nm recommended) Ti (~5 nm) + Au (75-100 nm recommended) Cr (~5 nm) + Au (75-100 nm recommended) TiW Cr
Comment		Stress in Wordentec Ni films: study here.		May use high-strength magnet for deposition.	May use high-strength magnet for deposition	Sample must be compatible with plating bath (pH = 3,65 and T = 52°C). Seed metal necessary.

* To deposit a cumulative thickness above 600 nm permission is required from metal@nanolab.dtu.dk to ensure enough material is present in the machine

** To deposit a cumulative thickness above 200 nm permission is required from metal@nanolab.dtu.dk to ensure enough material is present in the machine