Specific Process Knowledge/Thin film deposition/Deposition of Platinum: Difference between revisions
No edit summary |
No edit summary |
||
| Line 8: | Line 8: | ||
{| border="1" cellspacing="0" cellpadding="4" | {| border="1" cellspacing="0" cellpadding="4" | ||
|-style="background:silver; color:black" | |||
! | ! | ||
! E-beam evaporation ([[Specific Process Knowledge/Thin film deposition/Alcatel|Alcatel]]) | ! E-beam evaporation ([[Specific Process Knowledge/Thin film deposition/Alcatel|Alcatel]]) | ||
| Line 13: | Line 14: | ||
! Sputter deposition ([[Specific Process Knowledge/Thin film deposition/Lesker|Lesker]]) | ! Sputter deposition ([[Specific Process Knowledge/Thin film deposition/Lesker|Lesker]]) | ||
|- | |- | ||
| Batch size | |-style="background:WhiteSmoke; color:black" | ||
! Batch size | |||
| | | | ||
*Up to 1x4" wafers | *Up to 1x4" wafers | ||
| Line 26: | Line 28: | ||
*smaller pieces | *smaller pieces | ||
|- | |- | ||
| Pre-clean | |-style="background:LightGrey; color:black" | ||
! Pre-clean | |||
|RF Ar clean | |RF Ar clean | ||
|RF Ar clean | |RF Ar clean | ||
|RF Ar clean | |RF Ar clean | ||
|- | |- | ||
| Layer thickness | |-style="background:WhiteSmoke; color:black" | ||
! Layer thickness | |||
|10Å to 5000Å* | |10Å to 5000Å* | ||
|10Å to 5000Å* | |10Å to 5000Å* | ||
|10Å to 5000Å | |10Å to 5000Å | ||
|- | |- | ||
| Deposition rate | |-style="background:LightGrey; color:black" | ||
! Deposition rate | |||
|2Å/s to 15Å/s | |2Å/s to 15Å/s | ||
|10Å/s to 15Å/s | |10Å/s to 15Å/s | ||
|? Å/s to ? Å/s | |? Å/s to ? Å/s | ||
|- | |- | ||
|-style="background:WhiteSmoke; color:black" | |||
!Allowed materials | |||
| | |||
* Silicon | |||
* Silicon oxide | |||
* Silicon (oxy)nitride | |||
* Photoresist | |||
* PMMA | |||
* Mylar | |||
* SU-8 | |||
* Metals | |||
| | |||
* Silicon | |||
* Silicon oxide | |||
* Silicon (oxy)nitride | |||
* Photoresist | |||
* PMMA | |||
* Mylar | |||
* SU-8 | |||
* Metals | |||
| | |||
* Silicon | |||
* Silicon oxide | |||
* Silicon nitride | |||
* Silicon (oxy)nitride | |||
* Photoresist | |||
* PMMA | |||
* Mylar | |||
* SU-8 | |||
* Metals | |||
* Carbon | |||
|-style="background:LightGrey; color:black" | |||
! Comment | |||
| | |||
| | |||
| | |||
|} | |} | ||
'''*''' ''For thicknesses above 200 nm permission is required from Thin Film group.'' | '''*''' ''For thicknesses above 200 nm permission is required from Thin Film group.'' | ||
Revision as of 09:19, 10 March 2014
Feedback to this page: click here
Platinum deposition
Platinum can be deposited by e-beam evaporation. In the chart below you can compare the different deposition equipment.
| E-beam evaporation (Alcatel) | E-beam evaporation (Wordentec) | Sputter deposition (Lesker) | |
|---|---|---|---|
| Batch size |
|
|
|
| Pre-clean | RF Ar clean | RF Ar clean | RF Ar clean |
| Layer thickness | 10Å to 5000Å* | 10Å to 5000Å* | 10Å to 5000Å |
| Deposition rate | 2Å/s to 15Å/s | 10Å/s to 15Å/s | ? Å/s to ? Å/s |
| Allowed materials |
|
|
|
| Comment |
* For thicknesses above 200 nm permission is required from Thin Film group.