=SiO2 test - 5 jan 2024= | |||
{| border="1" cellspacing="1" cellpadding="1 | * The SiO2 layer deposited was 2um, deposited on the C1 furnace (recipe: WET1100, 12h40+00:20). | ||
* They were patterned with 915 UVN resist (DUV negative) and 65nm of BARC. | |||
* The following results were processed on chips (2*2cm) bonded to a 100mm dummy wafer. | |||
<br> | |||
{| border="1" cellspacing="1" cellpadding="1" | |||
! '''Recipe''' | ! '''Recipe''' | ||
! ''' | ! '''Time (min)''' | ||
! '''Date''' | ! '''Date''' | ||
! '''SEM picture''' | ! '''SEM picture''' | ||
! '''Etch rate SiO2 (nm/min)''' | |||
! '''Etch rate | ! '''Etch rate resist (nm/min)''' | ||
! '''Etch rate | |||
! '''Selectivity <br> (SiO2:resist)''' | ! '''Selectivity <br> (SiO2:resist)''' | ||
|- | |- | ||
|- | |- | ||
|-style="background:white; color:black" | |-style="background:white; color:black" | ||
|<!-- '''Recipe name''' --> '''CHF3_t1''' | |<!-- '''Recipe name''' --> '''CHF3_t1'''<br> CHF<sub>3</sub>= 22.5 sccm <br> H<sub>2</sub>= 22.5 sccm <br> Coil= 800W <br> Platen= '''30W''' <br> Press= 2.5mTorr <br> Temp= 20°C <br> | ||
|<!--Process time--> 10:00 | |||
|<!--Process time--> | |<!--'''Date'''--> 25/01 <br>-2024 | ||
|<!--'''Date'''--> | |<!--'''SEM picture'''--> [[File:25.01 CHF3.t1 30w 10m-01.png|250px]] [[File:25.01 CHF3.t1 30w 10m-02.png|250px]] [[File:25.01 CHF3.t1 30w 10m-03.png|250px]] [[File:25.01 CHF3.t1 30w 10m-04.png|250px]] | ||
|<!--'''SEM picture'''--> [[File: | |<!--'''Etch rate in SiO2'''--> 250nm- 61,99 <br> <br> 500nm- 68,12 <br> <br> 1000nm- 74,7 <br> <br> 2000nm- 76,55 | ||
|<!--'''Etch rate in resist'''--> 250nm- 61,31 <br> <br> 500nm- 49,85 <br> <br> 1000nm- 46,83 <br> <br> 2000nm- 47,3 | |||
|<!--'''Etch rate in SiO2'''--> | |<!--'''Selectivity (SiO2:resist)'''--> 250nm- 1,01 <br> <br> 500nm- 1,37 <br> <br> 1000nm- 1,6 <br> <br> 2000nm- 1,62 | ||
|<!--'''Etch rate in resist'''--> | |||
|<!--'''Selectivity (SiO2:resist)'''--> | |||
|- | |- | ||
|- | |- | ||
|-style="background:white; color:black" | |-style="background:white; color:black" | ||
|<!-- '''Recipe name''' --> | |<!-- '''Recipe name''' --> '''CHF3_t1''' <br> CHF<sub>3</sub>= 22.5 sccm <br> H<sub>2</sub>= 22.5 sccm <br> Coil= 150W <br> Platen= '''45W''' <br> Press= 2.5mTorr <br> Temp= 20°C <br> | ||
|<!--'''Process time'''--> 10:00 | |||
|<!--'''Date'''--> 25/01<br>-2024 | |||
|<!--'''Process time'''--> | |<!--'''SEM picture'''--> [[File:25.01 CHF3.t1 45w 10m-02.png|250px]] [[File:25.01 CHF3.t1 45w 10m-03.png|250px]] [[File:25.01 CHF3.t1 45w 10m-04.png|250px]] [[File:25.01 CHF3.t1 45w 10m-05.png|250px]] | ||
|<!--'''Date'''--> | |<!--'''Etch rate in SiO2'''--> 250nm- 90,74 <br> <br> 500nm- 84,63 <br> <br> 1000nm- 89,33 <br> <br> 2000nm- 94,34 | ||
|<!--'''SEM picture'''--> | |<!--'''Etch rate in resist'''--> 250nm- 81,1 <br> <br> 500nm- 53,77 <br> <br> 1000nm- 52,23 <br> <br> 2000nm- 54,81 | ||
| | |<!--'''Selectivity (SiO2:resist)'''--> 250nm- 1,12 <br> <br> 500nm- 1,57 <br> <br> 1000nm- 1,71 <br> <br> 2000nm- 1,72 | ||
|<!--'''Etch rate in SiO2'''--> | |- | ||
|<!--'''Etch rate in resist'''--> | |||
|<!--'''Selectivity (SiO2:resist)'''--> | |||
|- | |||
|- | |- | ||
|-style="background:white; color:black" | |-style="background:white; color:black" | ||
|<!-- '''Recipe name''' --> '''CHF3_t2''' | |<!-- '''Recipe name''' --> '''CHF3_t2''' <br> CF<sub>4</sub>= 22.5 sccm <br> H<sub>2</sub>= 22.5 sccm <br> Coil= 150W <br> Platen= '''45W''' <br> Press= 2.5mTorr <br> Temp= 20°C <br> | ||
|<!--'''Process time'''--> 15:00 | |||
|<!--'''Process time'''--> | |<!--'''Date'''--> 25/01<br>-2024 | ||
|<!--'''Date'''--> | |<!--'''SEM picture'''--> [[File:25.01 CHF3.t2 45w 15m-01.png|250px]] [[File:25.01 CHF3.t2 45w 15m-02.png|250px]] [[File:25.01 CHF3.t2 45w 15m-03.png|250px]] [[File:25.01-CHF3.t2-45w-15m-04.png|250px]] <br> *it's visible that redeposits, so the ER and selectivity may not be correct. | ||
|<!--'''SEM picture'''--> [[File: | |<!--'''Etch rate in SiO2'''-->250nm- 9,18 <br> <br>500nm- 22,46 <br> <br>1000nm- 28,03 <br> <br>2000nm- 28,75 | ||
|<!--'''Etch rate in resist'''-->250nm- 11,09 <br> <br>500nm- 3,96 <br> <br>1000nm- 4,22 <br> <br>2000nm- 4,40 | |||
|<!--'''Etch rate in SiO2'''--> | |<!--'''Selectivity (SiO2:resist)'''-->250nm- 0,83 <br> <br>500nm- 5,67 <br> <br>1000nm- 6,64 <br> <br>2000nm- 6,5 | ||
|<!--'''Etch rate in resist'''--> | |||
|<!--'''Selectivity (SiO2:resist)'''--> | |||
|- | |- | ||
|- | |- | ||
| | |} | ||
| | <br> | ||
<br clear="all" /> | |||
=Etch test of Silicon Nitride= | |||
* The nitride layer deposited was 560nm, on the PECVD4 (recipe: Standard HF SiN with wafer clean, for 1h). <br> | |||
* They were patterned with 750 DUV resist and 65nm of BARC (exposure:355 J/m2, focus:-3.1). <br> | |||
* The following results were processed on chips (2*2cm) bonded to a 100mm dummy wafer. | |||
{| border="1" cellspacing="1" cellpadding="1" | |||
! '''Recipe''' | |||
! '''Time (min)''' | |||
! '''Date''' | |||
! '''SEM picture''' | |||
! '''Redeposition - top view''' | |||
! '''Etch rate SiN (nm/min)''' | |||
! '''Etch rate resist (nm/min)''' | |||
! '''Selectivity <br> (SiN:resist)''' | |||
|- | |- | ||
|- | |- | ||
|-style="background:white; color:black" | |-style="background:white; color:black" | ||
|<!-- '''Recipe name''' --> ''' | |<!-- '''Recipe name''' --> '''CHF3_t1''' <br> CHF<sub>3</sub>= 22.5 sccm <br> H<sub>2</sub>= 22.5 sccm <br> Coil= 800W <br> Platen= 15W <br> Press= 2.5mTorr <br> Temp= 20°C <br> | ||
|<!--Process time--> 2:30 | |||
|<!-- | |<!--'''Date'''--> 29/02 <br>-2024 | ||
|<!--'''Date'''--> 29/02 | |<!--'''SEM picture'''--> [[File:Si3N4-pat1-chf3t1-250.png|170px]] [[File:Si3N4-pat1-chf3t1-500.png|170px]] [[File:Si3N4-pat1-chf3t1-1000.png|170px]] [[File:Si3N4-pat1-chf3t1-2000.png|170px]] | ||
|<!--'''SEM picture'''--> | |<!--'''Redeposition- side view''--> [[File:SiN chf3.t1 sidewalls 01.png|170px]] [[File:SiN chf3.t1 sidewalls 02.png|170px]] | ||
|<!--'''Redeposition - | |<!--'''Etch rate in SiO2'''--> 250nm- 155,08 <br> <br> 500nm- 170,32 <br> <br> 1000nm- 174,45 <br> <br> 2000nm- 179,76 | ||
|<!--'''Etch rate in SiO2'''--> | |<!--'''Etch rate in resist'''--> 250nm- 65,52 <br> <br> 500nm- 56,36 <br> <br> 1000nm- 64,56 <br> <br> 2000nm- 68,84 | ||
|<!--'''Etch rate in resist'''--> | |<!--'''Selectivity (SiO2:resist)'''--> 250nm- 2,37 <br> <br> 500nm- 3,02 <br> <br> 1000nm- 2,70 <br> <br> 2000nm- 2,61 | ||
|<!--'''Selectivity (SiO2:resist)'''--> | |||
|- | |- | ||
|- | |- | ||
|-style="background:white; color:black" | |-style="background:white; color:black" | ||
|<!-- '''Recipe name''' --> | |<!-- '''Recipe name''' --> '''CHF3_t2''' <br> CHF<sub>3</sub>= 22.5 sccm <br> H<sub>2</sub>= 22.5 sccm <br> Coil= 150W <br> Platen= '''45W''' <br> Press= 2.5mTorr <br> Temp= 20°C <br> | ||
|<!--'''Process time'''--> 5:00 | |||
|<!--'''Process time'''--> | |<!--'''Date'''--> 29/02<br>-2024 | ||
|<!--'''Date'''--> | |<!--'''SEM picture'''--> [[File:Si3N4-pat2-chf3t2-250.png|170px]] [[File:Si3N4-pat2-chf3t2-500.png|170px]] [[File:Si3N4-pat2-chf3t2-1000.png|170px]] [[File:Si3N4-pat2-chf3t2-2000.png|170px]] | ||
|<!--'''SEM picture'''--> | |<!--'''Redeposition - top view'''--> [[File:SiN chf3.t2 sidewalls 01.png|170px]] [[File:SiN chf3.t2 sidewalls 02.png|170px]] | ||
|<!--'''Redeposition - top view'''--> | |<!--'''Etch rate in SiO2'''--> 250nm- 28,12 <br> <br> 500nm- 41,86 <br> <br> 1000nm- 66 <br> <br> 2000nm- 63,62 | ||
|<!--'''Etch rate in SiO2'''--> | |<!--'''Etch rate in resist'''--> 250nm- 23,26 <br> <br> 500nm- 22,60 <br> <br> 1000nm- 16,74 <br> <br> 2000nm- 15,34 | ||
|<!--'''Etch rate in resist'''--> | |<!--'''Selectivity (SiO2:resist)'''--> 250nm- 1.21 <br> <br> 500nm- 1.85 <br> <br> 1000nm- 3.94 <br> <br> 2000nm- 4.15 | ||
|<!--'''Selectivity (SiO2:resist)'''--> | |||
|- | |- | ||
|- | |- |
Latest revision as of 12:37, 29 April 2024
Tests performed with UV resist:
The tests were performed on a 100mm wafer patterned on MLA3, with 2.2um AZ5214E resist.
Tests performed with DUV resist:
The resist used was a negative DUV resist (UVN) with 915nm + 88nm BARC layer.
SiO2 test - 5 jan 2024
- The SiO2 layer deposited was 2um, deposited on the C1 furnace (recipe: WET1100, 12h40+00:20).
- They were patterned with 915 UVN resist (DUV negative) and 65nm of BARC.
- The following results were processed on chips (2*2cm) bonded to a 100mm dummy wafer.
Etch test of Silicon Nitride
- The nitride layer deposited was 560nm, on the PECVD4 (recipe: Standard HF SiN with wafer clean, for 1h).
- They were patterned with 750 DUV resist and 65nm of BARC (exposure:355 J/m2, focus:-3.1).
- The following results were processed on chips (2*2cm) bonded to a 100mm dummy wafer.