Specific Process Knowledge/Etch/Etching of Silicon Oxide/SiO2 etch using ASE/tests CHF3+H2: Difference between revisions
Jump to navigation
Jump to search
(109 intermediate revisions by the same user not shown) | |||
Line 1: | Line 1: | ||
Tests performed with AZ5214E resist | =Tests performed with UV resist:= | ||
The tests were performed on a 100mm wafer patterned on MLA3, with 2.2um AZ5214E resist. | |||
{| border="1" cellspacing="1" cellpadding="1" align="left" | {| border="1" cellspacing="1" cellpadding="1" align="left" | ||
! '''Recipe''' | ! '''Recipe''' | ||
! '''Recipe parameters''' | ! '''Recipe parameters''' | ||
! ''' | ! '''Duration (min)''' | ||
! '''Date''' | ! '''Date''' | ||
! '''SEM picture''' | ! '''SEM picture''' | ||
Line 13: | Line 15: | ||
! '''Etch rate in resist <br> (AZ5214E inverse)''' | ! '''Etch rate in resist <br> (AZ5214E inverse)''' | ||
! '''Selectivity <br> (SiO2:resist)''' | ! '''Selectivity <br> (SiO2:resist)''' | ||
|- | |- | ||
|- | |- | ||
Line 19: | Line 20: | ||
|<!-- '''Recipe name''' --> CHF3_t1 | |<!-- '''Recipe name''' --> CHF3_t1 | ||
|<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= '''22.5''' sccm <br> Coil= 800W <br> Platen= 15W <br> Press= 2.5mTorr <br> Temp= 20°C <br> | |<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= '''22.5''' sccm <br> Coil= 800W <br> Platen= 15W <br> Press= 2.5mTorr <br> Temp= 20°C <br> | ||
|<!--'''Process time'''--> 12:00 | |<!--'''Process time'''--> 12:00 | ||
|<!--'''Date'''--> 04/09/2023 | |<!--'''Date'''--> 04/09/2023 | ||
|<!--'''SEM picture'''--> [[File:CHF3 t1 pat C 01.png|200px]] | |<!--'''SEM picture'''--> [[File:CHF3 t1 pat C 01.png|200px]] | ||
Line 27: | Line 28: | ||
|<!--'''Etch rate in resist'''--> 57.3 nm/min <br> +/- 12.9% | |<!--'''Etch rate in resist'''--> 57.3 nm/min <br> +/- 12.9% | ||
|<!--'''Selectivity (SiO2:resist)'''--> 1.22 | |<!--'''Selectivity (SiO2:resist)'''--> 1.22 | ||
|- | |- | ||
|- | |- | ||
Line 33: | Line 33: | ||
|<!-- '''Recipe name''' --> '''CHF3_t2''' | |<!-- '''Recipe name''' --> '''CHF3_t2''' | ||
|<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= 22.5 sccm <br> Coil= '''150W''' <br> Platen= '''25W''' <br> Press= 2.5mTorr <br> Temp= 20°C <br> | |<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= 22.5 sccm <br> Coil= '''150W''' <br> Platen= '''25W''' <br> Press= 2.5mTorr <br> Temp= 20°C <br> | ||
|<!--'''Process time'''--> 25:00 | |<!--'''Process time'''--> 25:00 | ||
|<!--'''Date'''--> 04/09/2023 | |<!--'''Date'''--> 04/09/2023 | ||
|<!--'''SEM picture'''--> [[File:CHF3 t2 pat C 05.png|200px]] | |<!--'''SEM picture'''--> [[File:CHF3 t2 pat C 05.png|200px]] | ||
Line 41: | Line 41: | ||
|<!--'''Etch rate in resist'''--> 24.2 nm/min <br> +/- 21.1% | |<!--'''Etch rate in resist'''--> 24.2 nm/min <br> +/- 21.1% | ||
|<!--'''Selectivity (SiO2:resist)'''--> 1.1 | |<!--'''Selectivity (SiO2:resist)'''--> 1.1 | ||
|- | |- | ||
|- | |- | ||
Line 47: | Line 46: | ||
|<!-- '''Recipe name''' --> '''CHF3 t2''' | |<!-- '''Recipe name''' --> '''CHF3 t2''' | ||
|<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= 22.5 sccm <br> '''H<sub>2</sub>= 22.5 sccm''' <br> Coil= 150W <br> Platen= 25W <br> Press= 2.5mTorr <br> Temp= 20°C <br> | |<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= 22.5 sccm <br> '''H<sub>2</sub>= 22.5 sccm''' <br> Coil= 150W <br> Platen= 25W <br> Press= 2.5mTorr <br> Temp= 20°C <br> | ||
|<!--'''Process time'''--> 10:00 | |<!--'''Process time'''--> 10:00 | ||
|<!--'''Date'''--> 22/09/2023 | |<!--'''Date'''--> 22/09/2023 | ||
|<!--'''SEM picture'''--> [[File:CHF3.t2-10H2-25min-C-01.png|200px]] | |<!--'''SEM picture'''--> [[File:CHF3.t2-10H2-25min-C-01.png|200px]] | ||
Line 55: | Line 54: | ||
|<!--'''Etch rate in resist'''--> 1,8 nm/min <br> +/- 46.5% | |<!--'''Etch rate in resist'''--> 1,8 nm/min <br> +/- 46.5% | ||
|<!--'''Selectivity (SiO2:resist)'''--> 5.4 | |<!--'''Selectivity (SiO2:resist)'''--> 5.4 | ||
|- | |- | ||
|- | |- | ||
Line 61: | Line 59: | ||
|<!-- '''Recipe name''' --> CHF3_t1 | |<!-- '''Recipe name''' --> CHF3_t1 | ||
|<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= '''22.5''' sccm <br> '''H<sub>2</sub>= 10''' sccm <br> Coil= 800W <br> Platen= 15W <br> Press= 2.5mTorr <br> Temp= 20°C <br> | |<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= '''22.5''' sccm <br> '''H<sub>2</sub>= 10''' sccm <br> Coil= 800W <br> Platen= 15W <br> Press= 2.5mTorr <br> Temp= 20°C <br> | ||
|<!--'''Process time'''--> 10:00 | |<!--'''Process time'''--> 10:00 | ||
|<!--'''Date'''--> 12/09/2023 | |<!--'''Date'''--> 12/09/2023 | ||
|<!--'''SEM picture'''--> [[File:CHF310 H2 10min 08.png|200px]] | |<!--'''SEM picture'''--> [[File:CHF310 H2 10min 08.png|200px]] | ||
Line 69: | Line 67: | ||
|<!--'''Etch rate in resist'''--> 47,5 nm/min <br> +/- 21.5% | |<!--'''Etch rate in resist'''--> 47,5 nm/min <br> +/- 21.5% | ||
|<!--'''Selectivity (SiO2:resist)'''--> 1.25 | |<!--'''Selectivity (SiO2:resist)'''--> 1.25 | ||
|- | |- | ||
|- | |- | ||
Line 75: | Line 72: | ||
|<!-- '''Recipe name''' --> CHF3_t1 | |<!-- '''Recipe name''' --> CHF3_t1 | ||
|<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= '''22.5''' sccm <br> '''O<sub>2</sub>= 10''' sccm <br> Coil= 800W <br> Platen= 15W <br> Press= 2.5mTorr <br> Temp= 20°C <br> | |<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= '''22.5''' sccm <br> '''O<sub>2</sub>= 10''' sccm <br> Coil= 800W <br> Platen= 15W <br> Press= 2.5mTorr <br> Temp= 20°C <br> | ||
|<!--'''Process time'''--> 10:00 | |<!--'''Process time'''--> 10:00 | ||
|<!--'''Date'''--> 11/09/2023 | |<!--'''Date'''--> 11/09/2023 | ||
|<!--'''SEM picture'''--> [[File:CHF310 O2 10min 01.png|200px]] | |<!--'''SEM picture'''--> [[File:CHF310 O2 10min 01.png|200px]] | ||
Line 83: | Line 80: | ||
|<!--'''Etch rate in resist'''--> 130,8 nm/min <br> +/- 8.8% | |<!--'''Etch rate in resist'''--> 130,8 nm/min <br> +/- 8.8% | ||
|<!--'''Selectivity (SiO2:resist)'''--> 0.46 | |<!--'''Selectivity (SiO2:resist)'''--> 0.46 | ||
|- | |- | ||
|- | |- | ||
Line 89: | Line 85: | ||
|<!-- '''Recipe name''' --> CHF3 t1 | |<!-- '''Recipe name''' --> CHF3 t1 | ||
|<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= '''22.5''' sccm <br> H<sub>2</sub>= '''22.5''' sccm <br> Coil= 800W <br> Platen= 15W <br> Press= 2.5mTorr <br> Temp= 20°C <br> | |<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= '''22.5''' sccm <br> H<sub>2</sub>= '''22.5''' sccm <br> Coil= 800W <br> Platen= 15W <br> Press= 2.5mTorr <br> Temp= 20°C <br> | ||
|<!--'''Process time'''--> 10:00 | |<!--'''Process time'''--> 10:00 | ||
|<!--'''Date'''--> 20/09/2023 | |<!--'''Date'''--> 20/09/2023 | ||
|<!--'''SEM picture'''--> [[File:CHF3=22.5 H2 10min C 01.png|200px]] | |<!--'''SEM picture'''--> [[File:CHF3=22.5 H2 10min C 01.png|200px]] | ||
Line 97: | Line 93: | ||
|<!--'''Etch rate in resist'''--> 26,4 nm/min <br> +/- 17,4% | |<!--'''Etch rate in resist'''--> 26,4 nm/min <br> +/- 17,4% | ||
|<!--'''Selectivity (SiO2:resist)'''--> 1.8 | |<!--'''Selectivity (SiO2:resist)'''--> 1.8 | ||
|- | |- | ||
|- | |- | ||
Line 103: | Line 98: | ||
|<!-- '''Recipe name''' --> CHF3 t1 | |<!-- '''Recipe name''' --> CHF3 t1 | ||
|<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= '''22.5''' sccm <br> H<sub>2</sub>= '''35''' sccm <br> Coil= 800W <br> Platen= 15W <br> Press= 2.5mTorr <br> Temp= 20°C <br> | |<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= '''22.5''' sccm <br> H<sub>2</sub>= '''35''' sccm <br> Coil= 800W <br> Platen= 15W <br> Press= 2.5mTorr <br> Temp= 20°C <br> | ||
|<!--'''Process time'''--> 10:00 | |<!--'''Process time'''--> 10:00 | ||
|<!--'''Date'''--> 22/09/2023 | |<!--'''Date'''--> 22/09/2023 | ||
|<!--'''SEM picture'''--> [[File:CHF3 35H2 10min C 02.png|200px]] | |<!--'''SEM picture'''--> [[File:CHF3 35H2 10min C 02.png|200px]] | ||
Line 111: | Line 106: | ||
|<!--'''Etch rate in resist'''--> 17,5 nm/min <br> +/- 13.9% | |<!--'''Etch rate in resist'''--> 17,5 nm/min <br> +/- 13.9% | ||
|<!--'''Selectivity (SiO2:resist)'''--> 2.09 | |<!--'''Selectivity (SiO2:resist)'''--> 2.09 | ||
|- | |- | ||
|- | |- | ||
Line 117: | Line 111: | ||
|<!-- '''Recipe name''' --> CHF3 t1 | |<!-- '''Recipe name''' --> CHF3 t1 | ||
|<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= '''35''' sccm <br> H<sub>2</sub>= '''35''' sccm <br> Coil= 800W <br> Platen= 15W <br> Press= 2.5mTorr <br> Temp= 20°C <br> | |<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= '''35''' sccm <br> H<sub>2</sub>= '''35''' sccm <br> Coil= 800W <br> Platen= 15W <br> Press= 2.5mTorr <br> Temp= 20°C <br> | ||
|<!--'''Process time'''--> 10:00 | |<!--'''Process time'''--> 10:00 | ||
|<!--'''Date'''--> 22/09/2023 | |<!--'''Date'''--> 22/09/2023 | ||
|<!--'''SEM picture'''--> [[File:CHF3 3535H2 10min E 01.png|200px]] | |<!--'''SEM picture'''--> [[File:CHF3 3535H2 10min E 01.png|200px]] | ||
Line 125: | Line 119: | ||
|<!--'''Etch rate in resist'''--> 23,8 nm/min <br> +/- 22.2% | |<!--'''Etch rate in resist'''--> 23,8 nm/min <br> +/- 22.2% | ||
|<!--'''Selectivity (SiO2:resist)'''--> 1.76 | |<!--'''Selectivity (SiO2:resist)'''--> 1.76 | ||
|- | |- | ||
|- | |- | ||
Line 131: | Line 124: | ||
|<!-- '''Recipe name''' --> CHF3 t1 | |<!-- '''Recipe name''' --> CHF3 t1 | ||
|<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= 22.5 sccm <br> '''CF<sub>4</sub>= 22.5''' sccm <br> Coil= 800W <br> Platen= 15W <br> Press= 2.5mTorr <br> Temp= 20°C <br> | |<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= 22.5 sccm <br> '''CF<sub>4</sub>= 22.5''' sccm <br> Coil= 800W <br> Platen= 15W <br> Press= 2.5mTorr <br> Temp= 20°C <br> | ||
|<!--'''Process time'''--> 10:00 | |<!--'''Process time'''--> 10:00 | ||
|<!--'''Date'''--> 22/09/2023 | |<!--'''Date'''--> 22/09/2023 | ||
|<!--'''SEM picture'''--> [[File:CHF3.t1 22.5CF4 10min C 01.png|200px]] | |<!--'''SEM picture'''--> [[File:CHF3.t1 22.5CF4 10min C 01.png|200px]] | ||
Line 139: | Line 132: | ||
|<!--'''Etch rate in resist'''--> 74,9 nm/min <br> +/- 10.8% | |<!--'''Etch rate in resist'''--> 74,9 nm/min <br> +/- 10.8% | ||
|<!--'''Selectivity (SiO2:resist)'''--> 1.01 | |<!--'''Selectivity (SiO2:resist)'''--> 1.01 | ||
|- | |- | ||
|- | |- | ||
Line 145: | Line 137: | ||
|<!-- '''Recipe name''' --> CHF3 t1 | |<!-- '''Recipe name''' --> CHF3 t1 | ||
|<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= '''22.5''' sccm <br> H<sub>2</sub>= '''22.5''' sccm <br> Coil= 800W <br> Platen= 15W <br> '''Press= 25mTorr''' <br> Temp= 20°C <br> | |<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= '''22.5''' sccm <br> H<sub>2</sub>= '''22.5''' sccm <br> Coil= 800W <br> Platen= 15W <br> '''Press= 25mTorr''' <br> Temp= 20°C <br> | ||
|<!--'''Process time'''--> 10:00 | |<!--'''Process time'''--> 10:00 | ||
|<!--'''Date'''--> 22/09/2023 | |<!--'''Date'''--> 22/09/2023 | ||
|<!--'''SEM picture'''--> [[File:CHF3.t122.5H2 25mT 10m C 04.png|200px]] | |<!--'''SEM picture'''--> [[File:CHF3.t122.5H2 25mT 10m C 04.png|200px]] | ||
Line 153: | Line 145: | ||
|<!--'''Etch rate in resist'''--> - | |<!--'''Etch rate in resist'''--> - | ||
|<!--'''Selectivity (SiO2:resist)'''--> no etch done,<br> polymer deposited | |<!--'''Selectivity (SiO2:resist)'''--> no etch done,<br> polymer deposited | ||
|- | |- | ||
|- | |- | ||
Line 159: | Line 150: | ||
|<!-- '''Recipe name''' --> CHF3 t1 | |<!-- '''Recipe name''' --> CHF3 t1 | ||
|<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= 22.5 sccm <br> H<sub>2</sub>= 22.5 sccm <br> Coil= 800W <br> Platen= 15W <br> Press= 2.5mTorr <br> '''Temp= 0°C''' <br> | |<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= 22.5 sccm <br> H<sub>2</sub>= 22.5 sccm <br> Coil= 800W <br> Platen= 15W <br> Press= 2.5mTorr <br> '''Temp= 0°C''' <br> | ||
|<!--'''Process time'''--> 10:00 | |<!--'''Process time'''--> 10:00 | ||
|<!--'''Date'''--> 22/09/2023 | |<!--'''Date'''--> 22/09/2023 | ||
|<!--'''SEM picture'''--> [[File:CHF3-22.5-H2-10min-0C-C-03.png|200px]] | |<!--'''SEM picture'''--> [[File:CHF3-22.5-H2-10min-0C-C-03.png|200px]] | ||
Line 167: | Line 158: | ||
|<!--'''Etch rate in resist'''--> 23,3 nm/min <br> +/- 13.7% | |<!--'''Etch rate in resist'''--> 23,3 nm/min <br> +/- 13.7% | ||
|<!--'''Selectivity (SiO2:resist)'''--> 2.06 | |<!--'''Selectivity (SiO2:resist)'''--> 2.06 | ||
|- | |- | ||
|- | |- | ||
Line 176: | Line 166: | ||
<br clear="all" /> | <br clear="all" /> | ||
=Tests performed with DUV resist:= | |||
The resist used was a negative DUV resist (UVN) with 915nm + 88nm BARC layer. | |||
{| border="1" cellspacing="1" cellpadding="1" align="left" | {| border="1" cellspacing="1" cellpadding="1" align="left" | ||
! '''Recipe''' | ! '''Recipe''' | ||
! '''Recipe parameters''' | ! '''Recipe parameters''' | ||
! ''' | ! '''Duration (min)''' | ||
! '''Date''' | ! '''Date''' | ||
! '''SEM picture''' | ! '''SEM picture''' | ||
! '''Etch rate in SiO2''' | ! '''Etch rate in SiO2''' | ||
! '''Etch rate in resist <br> ( | ! '''Etch rate in resist <br> (UVN)''' | ||
! '''Selectivity <br> (SiO2:resist)''' | ! '''Selectivity <br> (SiO2:resist)''' | ||
|- | |- | ||
|- | |- | ||
|-style="background:white; color:black" | |-style="background:white; color:black" | ||
|<!-- '''Recipe name''' --> CHF3_t1 | |<!-- '''Recipe name''' --> CHF3_t1 | ||
|<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= | |<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= 22.5 sccm <br> H<sub>2</sub>= 22.5 sccm <br> Coil= 800W <br> Platen= '''30W''' <br> Press= 2.5mTorr <br> Temp= 20°C <br> | ||
|<!--'''Process time'''--> | |<!--'''Process time'''--> 10:00 | ||
|<!--'''Date'''--> | |<!--'''Date'''--> 13/11/23 | ||
|<!--'''SEM picture'''--> [[File: | |<!--'''SEM picture'''--> [[File:nP CHF3_t1 22.5 10min 30WP-01.png|200px]] [[File:nP CHF3_t1 22.5 10min 30WP-03.png|200px]] | ||
|<!--''' | |<!--'''Etch rate in SiO2'''--> 47 | ||
|<!--'''Etch rate in SiO2'''--> | |<!--'''Etch rate in resist'''-->24.6 | ||
|<!--'''Etch rate in resist'''--> | |<!--'''Selectivity (SiO2:resist)'''--> 1.9 | ||
|<!--'''Selectivity (SiO2:resist)'''--> 1.22 | |- | ||
|<!--'''Etch rate in | |- | ||
|-style="background:white; color:black" | |||
|<!-- '''Recipe name''' --> CHF3_t1 | |||
|<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= 22.5 sccm <br> H<sub>2</sub>= 22.5 sccm <br> Coil= 800W <br> Platen= '''45W''' <br> Press= 2.5mTorr <br> Temp= 20°C <br> | |||
|<!--'''Process time'''--> 10:00 | |||
|<!--'''Date'''--> 13/11/23 | |||
|<!--'''SEM picture'''--> [[File:nP CHF3_t1 22.5 10min 45WP-01.png|200px]] [[File:nP CHF3_t1 22.5 10min 45WP-04.png|200px]] | |||
|<!--'''Etch rate in SiO2'''--> 59 | |||
|<!--'''Etch rate in resist'''--> 30 | |||
|<!--'''Selectivity (SiO2:resist)'''--> 1.9 | |||
|- | |||
|- | |||
|-style="background:white; color:black" | |||
|<!-- '''Recipe name''' --> CHF3_t1 | |||
|<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= 22.5 sccm <br> H<sub>2</sub>= 22.5 sccm <br> Coil= 800W <br> Platen= '''45W''' <br> Press= 2.5mTorr <br> Temp= '''0°C''' <br> | |||
|<!--'''Process time'''--> 10:00 | |||
|<!--'''Date'''--> 07/12/23 | |||
|<!--'''SEM picture'''--> [[File:CHF3_t1 0C 45W 01.png|300px]] | |||
|<!--'''Etch rate in SiO2'''--> 96 | |||
|<!--'''Etch rate in resist'''--> 56 | |||
|<!--'''Selectivity (SiO2:resist)'''--> 1.7 | |||
|- | |||
|- | |||
|-style="background:white; color:black" | |||
|<!-- '''Recipe name''' --> CHF3_t2 | |||
|<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= 22.5 sccm <br> H<sub>2</sub>= 22.5 sccm <br> Coil= 150W <br> Platen= 25W <br> Press= 2.5mTorr <br> Temp= 20°C <br> | |||
|<!--'''Process time'''--> '''10:00''' | |||
|<!--'''Date'''--> 23/10/23 | |||
|<!--'''SEM picture'''--> [[File:CHF_t2 nP 10min-05.png|300px]] | |||
|<!--'''Etch rate in SiO2'''--> 27 | |||
|<!--'''Etch rate in resist'''--> 12,5 | |||
|<!--'''Selectivity (SiO2:resist)'''--> 2.1 | |||
|- | |- | ||
|- | |- | ||
|-style="background:white; color:black" | |-style="background:white; color:black" | ||
|<!-- '''Recipe name''' --> | |<!-- '''Recipe name''' --> CHF3_t2 | ||
|<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= 22.5 sccm <br> Coil= | |<!-- '''SiO2 before etch''' --> CHF<sub>3</sub>= 22.5 sccm <br> H<sub>2</sub>= 22.5 sccm <br> Coil= 150W <br> Platen= 25W <br> Press= 2.5mTorr <br> Temp= 20°C <br> | ||
|<!--'''Process time'''--> | |<!--'''Process time'''--> '''20:00''' | ||
|<!--'''Date'''--> | |<!--'''Date'''--> 23/10/23 | ||
|<!--'''SEM picture'''--> [[File: | |<!--'''SEM picture'''--> [[File:CHF_t2 nP 20min-02.png|300px]] | ||
|<!--'''Etch rate in SiO2'''--> 8.15 | |||
|<!--'''Etch rate in SiO2'''--> | |<!--'''Etch rate in resist'''--> 7.5 | ||
|<!--'''Etch rate in resist'''--> | |||
|<!--'''Selectivity (SiO2:resist)'''--> 1.1 | |<!--'''Selectivity (SiO2:resist)'''--> 1.1 | ||
|- | |- | ||
|- | |- | ||
|} | |||
<br> | |||
<br clear="all" /> | |||
=SiO2 test - 5 jan 2024= | |||
* The SiO2 layer deposited was 2um, deposited on the C1 furnace (recipe: WET1100, 12h40+00:20). | |||
* They were patterned with 915 UVN resist (DUV negative) and 65nm of BARC. | |||
* The following results were processed on chips (2*2cm) bonded to a 100mm dummy wafer. | |||
<br> | |||
{| border="1" cellspacing="1" cellpadding="1" | |||
! '''Recipe''' | |||
! '''Time (min)''' | |||
! '''Date''' | |||
! '''SEM picture''' | |||
! '''Etch rate SiO2 (nm/min)''' | |||
! '''Etch rate resist (nm/min)''' | |||
! '''Selectivity <br> (SiO2:resist)''' | |||
|- | |||
|- | |||
|-style="background:white; color:black" | |||
|<!-- '''Recipe name''' --> '''CHF3_t1'''<br> CHF<sub>3</sub>= 22.5 sccm <br> H<sub>2</sub>= 22.5 sccm <br> Coil= 800W <br> Platen= '''30W''' <br> Press= 2.5mTorr <br> Temp= 20°C <br> | |||
|<!--Process time--> 10:00 | |||
|<!--'''Date'''--> 25/01 <br>-2024 | |||
|<!--'''SEM picture'''--> [[File:25.01 CHF3.t1 30w 10m-01.png|250px]] [[File:25.01 CHF3.t1 30w 10m-02.png|250px]] [[File:25.01 CHF3.t1 30w 10m-03.png|250px]] [[File:25.01 CHF3.t1 30w 10m-04.png|250px]] | |||
|<!--'''Etch rate in SiO2'''--> 250nm- 61,99 <br> <br> 500nm- 68,12 <br> <br> 1000nm- 74,7 <br> <br> 2000nm- 76,55 | |||
|<!--'''Etch rate in resist'''--> 250nm- 61,31 <br> <br> 500nm- 49,85 <br> <br> 1000nm- 46,83 <br> <br> 2000nm- 47,3 | |||
|<!--'''Selectivity (SiO2:resist)'''--> 250nm- 1,01 <br> <br> 500nm- 1,37 <br> <br> 1000nm- 1,6 <br> <br> 2000nm- 1,62 | |||
|- | |||
|- | |||
|-style="background:white; color:black" | |||
|<!-- '''Recipe name''' --> '''CHF3_t1''' <br> CHF<sub>3</sub>= 22.5 sccm <br> H<sub>2</sub>= 22.5 sccm <br> Coil= 150W <br> Platen= '''45W''' <br> Press= 2.5mTorr <br> Temp= 20°C <br> | |||
|<!--'''Process time'''--> 10:00 | |||
|<!--'''Date'''--> 25/01<br>-2024 | |||
|<!--'''SEM picture'''--> [[File:25.01 CHF3.t1 45w 10m-02.png|250px]] [[File:25.01 CHF3.t1 45w 10m-03.png|250px]] [[File:25.01 CHF3.t1 45w 10m-04.png|250px]] [[File:25.01 CHF3.t1 45w 10m-05.png|250px]] | |||
|<!--'''Etch rate in SiO2'''--> 250nm- 90,74 <br> <br> 500nm- 84,63 <br> <br> 1000nm- 89,33 <br> <br> 2000nm- 94,34 | |||
|<!--'''Etch rate in resist'''--> 250nm- 81,1 <br> <br> 500nm- 53,77 <br> <br> 1000nm- 52,23 <br> <br> 2000nm- 54,81 | |||
|<!--'''Selectivity (SiO2:resist)'''--> 250nm- 1,12 <br> <br> 500nm- 1,57 <br> <br> 1000nm- 1,71 <br> <br> 2000nm- 1,72 | |||
|- | |||
|- | |||
|-style="background:white; color:black" | |||
|<!-- '''Recipe name''' --> '''CHF3_t2''' <br> CF<sub>4</sub>= 22.5 sccm <br> H<sub>2</sub>= 22.5 sccm <br> Coil= 150W <br> Platen= '''45W''' <br> Press= 2.5mTorr <br> Temp= 20°C <br> | |||
|<!--'''Process time'''--> 15:00 | |||
|<!--'''Date'''--> 25/01<br>-2024 | |||
|<!--'''SEM picture'''--> [[File:25.01 CHF3.t2 45w 15m-01.png|250px]] [[File:25.01 CHF3.t2 45w 15m-02.png|250px]] [[File:25.01 CHF3.t2 45w 15m-03.png|250px]] [[File:25.01-CHF3.t2-45w-15m-04.png|250px]] <br> *it's visible that redeposits, so the ER and selectivity may not be correct. | |||
|<!--'''Etch rate in SiO2'''-->250nm- 9,18 <br> <br>500nm- 22,46 <br> <br>1000nm- 28,03 <br> <br>2000nm- 28,75 | |||
|<!--'''Etch rate in resist'''-->250nm- 11,09 <br> <br>500nm- 3,96 <br> <br>1000nm- 4,22 <br> <br>2000nm- 4,40 | |||
|<!--'''Selectivity (SiO2:resist)'''-->250nm- 0,83 <br> <br>500nm- 5,67 <br> <br>1000nm- 6,64 <br> <br>2000nm- 6,5 | |||
|- | |||
|- | |||
|} | |||
<br> | |||
<br clear="all" /> | |||
=Etch test of Silicon Nitride= | |||
* The nitride layer deposited was 560nm, on the PECVD4 (recipe: Standard HF SiN with wafer clean, for 1h). <br> | |||
* They were patterned with 750 DUV resist and 65nm of BARC (exposure:355 J/m2, focus:-3.1). <br> | |||
* The following results were processed on chips (2*2cm) bonded to a 100mm dummy wafer. | |||
{| border="1" cellspacing="1" cellpadding="1" | |||
! '''Recipe''' | |||
! '''Time (min)''' | |||
! '''Date''' | |||
! '''SEM picture''' | |||
! '''Redeposition - top view''' | |||
! '''Etch rate SiN (nm/min)''' | |||
! '''Etch rate resist (nm/min)''' | |||
! '''Selectivity <br> (SiN:resist)''' | |||
|- | |||
|- | |||
|-style="background:white; color:black" | |||
|<!-- '''Recipe name''' --> '''CHF3_t1''' <br> CHF<sub>3</sub>= 22.5 sccm <br> H<sub>2</sub>= 22.5 sccm <br> Coil= 800W <br> Platen= 15W <br> Press= 2.5mTorr <br> Temp= 20°C <br> | |||
|<!--Process time--> 2:30 | |||
|<!--'''Date'''--> 29/02 <br>-2024 | |||
|<!--'''SEM picture'''--> [[File:Si3N4-pat1-chf3t1-250.png|170px]] [[File:Si3N4-pat1-chf3t1-500.png|170px]] [[File:Si3N4-pat1-chf3t1-1000.png|170px]] [[File:Si3N4-pat1-chf3t1-2000.png|170px]] | |||
|<!--'''Redeposition- side view''--> [[File:SiN chf3.t1 sidewalls 01.png|170px]] [[File:SiN chf3.t1 sidewalls 02.png|170px]] | |||
|<!--'''Etch rate in SiO2'''--> 250nm- 155,08 <br> <br> 500nm- 170,32 <br> <br> 1000nm- 174,45 <br> <br> 2000nm- 179,76 | |||
|<!--'''Etch rate in resist'''--> 250nm- 65,52 <br> <br> 500nm- 56,36 <br> <br> 1000nm- 64,56 <br> <br> 2000nm- 68,84 | |||
|<!--'''Selectivity (SiO2:resist)'''--> 250nm- 2,37 <br> <br> 500nm- 3,02 <br> <br> 1000nm- 2,70 <br> <br> 2000nm- 2,61 | |||
|- | |||
|- | |||
|-style="background:white; color:black" | |||
|<!-- '''Recipe name''' --> '''CHF3_t2''' <br> CHF<sub>3</sub>= 22.5 sccm <br> H<sub>2</sub>= 22.5 sccm <br> Coil= 150W <br> Platen= '''45W''' <br> Press= 2.5mTorr <br> Temp= 20°C <br> | |||
|<!--'''Process time'''--> 5:00 | |||
|<!--'''Date'''--> 29/02<br>-2024 | |||
|<!--'''SEM picture'''--> [[File:Si3N4-pat2-chf3t2-250.png|170px]] [[File:Si3N4-pat2-chf3t2-500.png|170px]] [[File:Si3N4-pat2-chf3t2-1000.png|170px]] [[File:Si3N4-pat2-chf3t2-2000.png|170px]] | |||
|<!--'''Redeposition - top view'''--> [[File:SiN chf3.t2 sidewalls 01.png|170px]] [[File:SiN chf3.t2 sidewalls 02.png|170px]] | |||
|<!--'''Etch rate in SiO2'''--> 250nm- 28,12 <br> <br> 500nm- 41,86 <br> <br> 1000nm- 66 <br> <br> 2000nm- 63,62 | |||
|<!--'''Etch rate in resist'''--> 250nm- 23,26 <br> <br> 500nm- 22,60 <br> <br> 1000nm- 16,74 <br> <br> 2000nm- 15,34 | |||
|<!--'''Selectivity (SiO2:resist)'''--> 250nm- 1.21 <br> <br> 500nm- 1.85 <br> <br> 1000nm- 3.94 <br> <br> 2000nm- 4.15 | |||
|- | |||
|- | |||
|} | |||
<br clear="all" /> |
Latest revision as of 12:37, 29 April 2024
Tests performed with UV resist:
The tests were performed on a 100mm wafer patterned on MLA3, with 2.2um AZ5214E resist.
Tests performed with DUV resist:
The resist used was a negative DUV resist (UVN) with 915nm + 88nm BARC layer.
SiO2 test - 5 jan 2024
- The SiO2 layer deposited was 2um, deposited on the C1 furnace (recipe: WET1100, 12h40+00:20).
- They were patterned with 915 UVN resist (DUV negative) and 65nm of BARC.
- The following results were processed on chips (2*2cm) bonded to a 100mm dummy wafer.
Etch test of Silicon Nitride
- The nitride layer deposited was 560nm, on the PECVD4 (recipe: Standard HF SiN with wafer clean, for 1h).
- They were patterned with 750 DUV resist and 65nm of BARC (exposure:355 J/m2, focus:-3.1).
- The following results were processed on chips (2*2cm) bonded to a 100mm dummy wafer.