Specific Process Knowledge/Etch/DRIE-Pegasus/Pegasus-4/SiO2 Etch/Cr mask: Difference between revisions
< Specific Process Knowledge | Etch | DRIE-Pegasus | Pegasus-4 | SiO2 Etch
Jump to navigation
Jump to search
Line 465: | Line 465: | ||
</gallery> | </gallery> | ||
|- | |- | ||
| | | | ||
*Coil Power [W]:600 | |||
*Platen Power [W]: 50 | |||
*Platen temperature [<sup>o</sup>C]: 20 | |||
*H2 flow [sccm]:0 | |||
*O2 flow [sccm]: 10 | |||
*C<sub>4</sub>F<sub>8</sub> flow [sccm]: 6.5 | |||
*He flow [sccm]:100 | |||
*Pressure:Fully open APC valve (<2 mTorr) | |||
*Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A' | |||
| | | | ||
<gallery caption=" C10751: SiO2 etch with Cr mask on wafer piece on Si carrier 20 min etch, EM:0/0 H2:0sccm, C4F8:6.5sccm He:100sccm O2:10sccm, Pressure:?mTorr; platen power 50W, coil power:600W" perrow="7" widths="200px" heights="150px"> | <gallery caption=" C10751: SiO2 etch with Cr mask on wafer piece on Si carrier 20 min etch, EM:0/0 H2:0sccm, C4F8:6.5sccm He:100sccm O2:10sccm, Pressure:?mTorr; platen power 50W, coil power:600W" perrow="7" widths="200px" heights="150px"> | ||
Line 476: | Line 485: | ||
</gallery> | </gallery> | ||
|- | |- | ||
| | | | ||
*Coil Power [W]:300 | |||
*Platen Power [W]: 25 | |||
*Platen temperature [<sup>o</sup>C]: 20 | |||
*H2 flow [sccm]:0 | |||
*O2 flow [sccm]: 10 | |||
*C<sub>4</sub>F<sub>8</sub> flow [sccm]: 6.5 | |||
*He flow [sccm]:100 | |||
*Pressure:Fully open APC valve (<2 mTorr) | |||
*Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A' | |||
| | | | ||
<gallery caption=" C10752: SiO2 etch with Cr mask on wafer piece on Si carrier 30 min etch, EM:0/0 H2:0sccm, C4F8:6.5sccm He:100sccm O2:10sccm, Pressure:?mTorr; platen power 25W, coil power:300W" perrow="6" widths="200px" heights="150px"> | <gallery caption=" C10752: SiO2 etch with Cr mask on wafer piece on Si carrier 30 min etch, EM:0/0 H2:0sccm, C4F8:6.5sccm He:100sccm O2:10sccm, Pressure:?mTorr; platen power 25W, coil power:300W" perrow="6" widths="200px" heights="150px"> | ||
Line 487: | Line 505: | ||
</gallery> | </gallery> | ||
|- | |- | ||
| | | | ||
*Coil Power [W]:300 | |||
*Platen Power [W]: 25 | |||
*Platen temperature [<sup>o</sup>C]: 20 | |||
*H2 flow [sccm]:0 | |||
*O2 flow [sccm]: 10 | |||
*C<sub>4</sub>F<sub>8</sub> flow [sccm]: 6.5 | |||
*He flow [sccm]:100 | |||
*Pressure:Fully open APC valve (<2 mTorr) | |||
*Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A' | |||
| | | | ||
<gallery caption=" C10834: SiO2 etch with Cr mask on wafer piece on Si carrier 45 min etch, EM:0/0 H2:0sccm, C4F8:6.5sccm He:100sccm O2:10sccm, Pressure:?mTorr; platen power 25W, coil power:300W" perrow="6" widths="200px" heights="150px"> | <gallery caption=" C10834: SiO2 etch with Cr mask on wafer piece on Si carrier 45 min etch, EM:0/0 H2:0sccm, C4F8:6.5sccm He:100sccm O2:10sccm, Pressure:?mTorr; platen power 25W, coil power:300W" perrow="6" widths="200px" heights="150px"> | ||
Line 504: | Line 531: | ||
</gallery> | </gallery> | ||
|- | |- | ||
| | | | ||
*Coil Power [W]:300 | |||
*Platen Power [W]: 20 | |||
*Platen temperature [<sup>o</sup>C]: 20 | |||
*H2 flow [sccm]:0 | |||
*O2 flow [sccm]: 10 | |||
*C<sub>4</sub>F<sub>8</sub> flow [sccm]: 6.5 | |||
*He flow [sccm]:100 | |||
*Pressure:Fully open APC valve (<2 mTorr) | |||
*Electromagnetic coils (EM) 'outer coil' / 'inner coil':'0 A' / '0 A' | |||
| | | | ||
<gallery caption=" C10844: SiO2 etch with Cr mask on wafer piece on Si carrier 50 min etch, EM:0/0 H2:0sccm, C4F8:6.5sccm He:100sccm O2:10sccm, Pressure:?mTorr; platen power 20W, coil power:300W" perrow="6" widths="200px" heights="150px"> | <gallery caption=" C10844: SiO2 etch with Cr mask on wafer piece on Si carrier 50 min etch, EM:0/0 H2:0sccm, C4F8:6.5sccm He:100sccm O2:10sccm, Pressure:?mTorr; platen power 20W, coil power:300W" perrow="6" widths="200px" heights="150px"> |
Revision as of 14:35, 6 February 2024
Feedback to this page: click here
Unless otherwise stated, all content in this section was done by Berit Herstrøm, DTU Nanolab
SiO2 trench etching with Cr mask
Start parameters, variations noted in the gallery headline | Recipe name: no 10 with lower platen power |
---|---|
Coil Power [W] | 2500 |
Platen Power [W] | 200 |
Platen temperature [oC] | 20 |
H2 flow [sccm] | 25.6 |
C4F8 flow [sccm] | 25.6 |
He flow [sccm] | 448.7 |
Pressure | Fully open APC valve (8-9 mTorr) |
Electromagnetic coils (EM) 'outer coil' / 'inner coil' | '2 A' / '30 A' (PLEASE DO NOT RUN WITH THESE SETTINGS FOR MORE THAN 6 MIN) |
- 100 nm Cr mask etched in ICP metal with 500nm DUV neg resist (NUV 2300-0.5) and 65 nm barc.
Results
Temporary conclusions on how the process parameters affect the results in this study: | What process parameters affect the results? |
|
|
Profile SEM images
Recipe settings | SEM gallery |
---|---|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Profile, top view at tilted SEM images on 800 nm pitch and 50% duty cycle ( look at the Cr mask in top of the page
- SiO2 etch with Cr mask on full wafer 6 min etch
- SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch
- SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm
- SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, O2:5sccm
- SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:225sccm, Pressure:3.35mTorr
- SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:225sccm, Pressure:3.35mTorr; platen power 150W, coil power:1200W
- SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:215sccm O2:10sccm, Pressure:3.6mTorr; platen power 150W, coil power:1200W
- SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.6mTorr; platen power 150W, coil power:1200W
- SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:215sccm O2:10sccm, Pressure:3.6mTorr; platen power 150W, coil power:1800W
- SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.6mTorr; platen power 150W, coil power:1800W
- SiO2 etch with Cr mask on wafer piece on Si carrier 6 min etch, H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.6mTorr; platen power 100W, coil power:1200W
- SiO2 etch with Cr mask on wafer piece on Si carrier 14 min etch (PLEASE DO NOT REPEAT THIS LONG TIME), H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.6mTorr; platen power 100W, coil power:1200W
- SiO2 etch with Cr mask on wafer piece on Si carrier 10 min etch, H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.6mTorr; platen power 150W, coil power:1800W
- SiO2 etch with Cr mask on wafer piece on Si carrier 14 min etch, EM:0/0 H2:0sccm, C4F8:13sccm He:205sccm O2:20sccm, Pressure:3.9mTorr; platen power 100W, coil power:1200W, the mask is removed by plasma ashing on top view and tilted view