Specific Process Knowledge/Thin film deposition/PECVD/Doping: Difference between revisions

From LabAdviser
Jump to navigation Jump to search
 
(7 intermediate revisions by 2 users not shown)
Line 1: Line 1:
'''Feedback to this page''': '''[mailto:labadviser@danchip.dtu.dk?Subject=Feed%20back%20from%20page%20http://labadviser.danchip.dtu.dk/index.php/Specific_Process_Knowledge/Thin_film_deposition/PECVD/Doping  click here]'''  
'''Feedback to this page''': '''[mailto:labadviser@nanolab.dtu.dk?Subject=Feed%20back%20from%20page%20http://labadviser.nanolab.dtu.dk/index.php/Specific_Process_Knowledge/Thin_film_deposition/PECVD/Doping  click here]'''  


 
=<span style="color:#FF0000">This work has been done on PECVD2. PECVD2 has been decomissioned but we keep this information because we expect PECVD3 and PECVD4 to behave similar</span>=
 
 
=<span style="background:#FF2800">THIS PAGE IS UNDER CONSTRUCTION</span>[[image:Under_construction.png|200px]]=


==Boron-doping by use of BSG glass deposited in PECVD2==
==Boron-doping by use of BSG glass deposited in PECVD2==
Line 35: Line 32:


5 tests were made where only the B<sub>2</sub>H<sub>6</sub> flow was changed for each deposition (120sccm,130sccm,140sccm,160sccm,240sccm). All deposition times were 2 min, resulting in 440 nm Oxide.
5 tests were made where only the B<sub>2</sub>H<sub>6</sub> flow was changed for each deposition (120sccm,130sccm,140sccm,160sccm,240sccm). All deposition times were 2 min, resulting in 440 nm Oxide.
The wafers were annealed in Anneal Oxide Furnace (C1) at 1000°C for 85 min to drive in the boron and the oxide was subsequently etched in BHF. The wafers were then analyzed by SIMS and the results are shown in the figure below:
The wafers were annealed in Anneal Oxide Furnace (C1) at 1000°C for 85 min to drive in the boron and the oxide was subsequently etched in BHF.  
 
The wafers were then analyzed by SIMS and the results are shown in the figure below:




Line 70: Line 69:
|}
|}


3 tests were made where only the B<sub>2</sub>H<sub>6</sub> flow was changed for each deposition (120sccm,130sccm,140sccm,160sccm,240sccm). All deposition times were 2 min, resulting in 440 nm Oxide.
3 tests were made where only the B<sub>2</sub>H<sub>6</sub> flow was changed for each deposition (120sccm,130sccm,140sccm,160sccm,240sccm). All deposition times were 2 min, resulting in approximately 400nm Oxide.
 
The wafers were going through several annealing and oxidation step:
The wafers were going through several annealing and oxidation step:


Line 84: Line 84:


[[image:PECVD_Boron_doping_profiles.jpg|627x424px|left|thumb|Boron concentration measured by SIMS. Results from Trine Holm Christensen, Space, Feb. 2015.]]
[[image:PECVD_Boron_doping_profiles.jpg|627x424px|left|thumb|Boron concentration measured by SIMS. Results from Trine Holm Christensen, Space, Feb. 2015.]]
<br clear="all" />


Measured peak concentrations and sheet resistances:
Measured peak concentrations and sheet resistances:
 
<br>
{| border="1" cellspacing="0" cellpadding="7" with="50" style="text-align:center;"
{| border="1" cellspacing="0" cellpadding="7" with="50" style="text-align:center;"
|-
|-

Latest revision as of 15:08, 7 August 2023

Feedback to this page: click here

This work has been done on PECVD2. PECVD2 has been decomissioned but we keep this information because we expect PECVD3 and PECVD4 to behave similar

Boron-doping by use of BSG glass deposited in PECVD2

Results from Joachim Dahl Thomsen, Nanotech, 2014

Recipe

Recipe name SiH4 flow [sccm] N2O flow [sccm] N2 flow [sccm] B2H6 flow [sccm] PH3 flow [sccm] Pressure [mTorr] Power [W] Description
1PBSG 17 1600 0 120, 130, 140, 160, 240 0 400 380 BSG glass for driving in boron in Silicon

5 tests were made where only the B2H6 flow was changed for each deposition (120sccm,130sccm,140sccm,160sccm,240sccm). All deposition times were 2 min, resulting in 440 nm Oxide. The wafers were annealed in Anneal Oxide Furnace (C1) at 1000°C for 85 min to drive in the boron and the oxide was subsequently etched in BHF.

The wafers were then analyzed by SIMS and the results are shown in the figure below:


Boron concentration measured by SIMS. Results from Joachim Dahl Thomsen, Nanotech, 2014.


Boron-doping by use of BSG glass deposited in PECVD2

Results from Trine Holm Christensen, Space, Feb. 2015

Recipe

Recipe name SiH4 flow [sccm] N2O flow [sccm] N2 flow [sccm] B2H6 flow [sccm] PH3 flow [sccm] Pressure [mTorr] Power [W] Description
1PBSG 17 1600 0 120, 130, 140 0 400 380 BSG glass for driving in boron in Silicon

3 tests were made where only the B2H6 flow was changed for each deposition (120sccm,130sccm,140sccm,160sccm,240sccm). All deposition times were 2 min, resulting in approximately 400nm Oxide.

The wafers were going through several annealing and oxidation step:

The total thermal budget for the wafers:

Anneal in Furnace (C1): ANN1000, 30 min in N2, strip of oxide in a 25 min BHF etch.

Wet oxidation in Furnace (C1): WET1050, 30 min, no further anneal

Anneal in Furnace (C1): ANN950, 60 min in N2

The wafers were then analyzed by SIMS and the results are shown in the figure below:

Boron concentration measured by SIMS. Results from Trine Holm Christensen, Space, Feb. 2015.


Measured peak concentrations and sheet resistances:

Wafer Peak Concentration

[atoms/cm3]

Sheet Resistance

[Ω/sq]

BSG120 1.75*1019 56.4
BSG130 2.44*1019 36.2
BSG140 2.36*1019 40.3