Specific Process Knowledge/Lithography/EBeamLithography/eLINE

THIS PAGE IS UNDER CONSTRUCTION

Process information for the Raith eLINE Plus system

The system was installed in the cleanroom in May 2022. As we get more familiar with the tool this page will be populated with relevant process information.

System overview

4 inch wafer holder and 100 mm Universal Sample Holder (USH)

The system is a dual use SEM and EBL exposure tool. For SEM applications the most notable difference from our other SEM's is the automation functionality that allows users to link a design to a substrate and simply from the design define areas to image and the tool will then image those areas without further user input. Once an imaging routine has been setup several hundred images can be acquired per hour. For a brief introduction to this feature see more in this video.

For EBL the system is a variable voltage exposure tool with a maximum acceleration voltage of 30 kV and beam currents from 0.01 to 12.6 nA. The stage position is controlled by a laser interferometer and has a position accuracy of about 1 nm.

Currently two holders are available, a 4" wafer holder and a 100 mm Universal Sample Holder (USH) for substrates up to about 75x75 mm. Chips can be clamped on either of the 8 chip clamps on the USH. The sample holders will rest on three ceramic balls on the stage, each ceramic ball fits into one of the kinematic mounts of the sample holder. The kinematic mounts are adjusted to keep the sample holder as level as possible. When handling the sample holders it is important not to touch the kinematic mounts.

Dose information

Base doses for exposure must be defined in the Pattern Parameter Calculation window.

The eLINE tool operates with four different design element types; area, curved elements, line and dot. The element types are classified as:

• Area: Polygons
• Curved elements: Elements that have an adjustable radius
• Line: Zero-width line
• Dot: Single point/vertice element

The software allows the user to define different doses for the four different types of elements and thus it is essential to know how the design is drawn and interpreted. The units used are:

• Area dose [µC/cm2],
• Curved element dose [µC/cm2]
• Line dose [pC/cm]
• Dot dose [pC].

Also notice that the unit prefix changes from micro to pico. We recommend setting the same dose for area and curved elements.

The dose for each type can be setup under the "Patterning Parameter". Before updating the requested dose the beam current must be measured from the "Patterning Parameter" page. In all tabs the user will set a step size, i.e. the distance between beam positions and a dose. The dwell time must then be updated by clicking the calculate icon next to the dwell time field. The dwell time will be calculated based on the last beam current measurement.

Dot dose, line dose and curved element doses can be disabled in the Patterning Parameter window and in that case the system will IGNORE the type of elements that are disabled, i.e. they will not be written.

We recommend all EBL users to do a dose test prior to exposing samples of significant value. As a starting point you can consider to use the Demo.csf provided on the tool. This pattern is available in the auto generated user folder. The pattern consist of areas, curved elements, lines and dots as shown below.

Overview image of the dose test design provided on the tool.

Table of dose to clear (area or curved elements) on Si substrate

The following table is merely at guideline to as to what sort of dose requirements to expect. Actual dose for your design will depend on substrate type and material, resist thickness, acceleration voltage, pattern density (proximity effects) and several other factors and thus users should always do a dose test with their actual pattern. Be aware that AR-N 8200 is in particular very dependent on PEB processing parameters. Refer to AR-N 8200 page for more information.

Dose [µC/cm2]
Acc. voltage	AR-P 6200.09 (180 nm)	PMMA 950k	AR-N 8200.06
10 kV	30	-	-
20 kV	70	-	-
30 kV	100	-	180

Typical beam currents

Beam current is a function of acceleration voltage and aperture and thus beam current is locked by the choice of acceleration voltage and aperture. Typical beam currents are given in the table below. Writing time can be estimated in the software once a job is defined, it is however straight forward to estimate in advance based on area to pattern, A, dose to clear, d0, and beam current, I as: T = d0*A/I

Notice that this estimate is only the beam dwell time and does not account for beam settling time or stage movement time. Typically process times are 3-4 times higher than the dwell time estimate but this will vary with pattern and writing conditions.

The High Current (HC) mode can be activated in the Column Control panel.

Typical beam current [nA] as function of acceleration voltage and aperture
Acc. voltage / Aperture	7 µm	10 µm	15 µm	20 µm	30 µm	60 µm	120 µm
10 kV	0.01	0.02	0.06	0.10	0.23	0.99	3.87
10 kV HC	0.02	0.05	0.12	0.20	0.39	1.96	7.67
20 kV	0.02	0.04	0.09	0.16	0.36	1.53	6.06
20 kV HC	0.03	0.08	0.18	0.32	0.61	3.03	11.9
30 kV	0.02	0.04	0.10	0.17	0.38	1.65	6.53
30 kV HC	0.04	0.09	0.19	0.34	0.64	3.20	12.6

Writing fields

Writefield dimension is a trade off between beam shot precision and field stitching. The maximum writefield size is 1000x1000 µm. The beam controller has a limit of 50000 addressable positions along each axis and hence for a 1000x1000 µm writefield the minimum beam pitch is 20 nm. For a 100x100 µm writefield the minimum beam pitch is 2 nm. Thus the precision is higher for smaller writing fields. Smaller writing fields will however fracture a design into more fields and create more field boundaries with higher potential for stitching errors.